Refractory Technology Periclase refractory contains mainly Al2O₃ MgO SiO₂ CaO Al2O₃ MgO SiO₂ CaO ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Addition of grog in fireclay brick during its manufacture is advantageous, because it results in Less addition of water to get a workable plasticity & lesser time required for drying the raw refractories and hence increased rate of production All of these High strength & thermal spalling resistance Less shrinkage in heating, decreased apparent porosity & increased specific gravity Less addition of water to get a workable plasticity & lesser time required for drying the raw refractories and hence increased rate of production All of these High strength & thermal spalling resistance Less shrinkage in heating, decreased apparent porosity & increased specific gravity ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Bauxite calcining rotary kilns are lined with __________ bricks. Fireclay Carbon Corundum 85% alumina Fireclay Carbon Corundum 85% alumina ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Spalling resistance of a refractory can not be increased by Using a coarser grog during its manufacture Decreasing its thermal co-efficient of expansion Increasing its porosity Making it denser Using a coarser grog during its manufacture Decreasing its thermal co-efficient of expansion Increasing its porosity Making it denser ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Presence of MgO in alumino-silicate refractories __________ its refractoriness. Either A or B; depends on its quantity Lowers Does not affect Increases Either A or B; depends on its quantity Lowers Does not affect Increases ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Refractoriness under load (RUL) of fireclay bricks (under a load of 2 kg/cm² ) is __________ °C. >2000 1000 >1350 500 >2000 1000 >1350 500 ANSWER DOWNLOAD EXAMIANS APP