Workshop Technology The purpose of a gate is to Feed the molten metal to the casting in order to compensate for the shrinkage Act as a reservoir for the molten metal Delivers molten metal from pouring basin to gate Delivers molten metal into the mould cavity Feed the molten metal to the casting in order to compensate for the shrinkage Act as a reservoir for the molten metal Delivers molten metal from pouring basin to gate Delivers molten metal into the mould cavity ANSWER DOWNLOAD EXAMIANS APP
Workshop Technology The temperature of oxy-hydrogen flame is ________ oxyacetylene flame. Less than Same as None of these More than Less than Same as None of these More than ANSWER DOWNLOAD EXAMIANS APP
Workshop Technology For welding plates of thickness less than 5 mm, its edges Do not require bevelling Should have a double-V or U-groove on one side Should have a double-V or U-groove on both sides Should be bevelled to a single-V or U-groove Do not require bevelling Should have a double-V or U-groove on one side Should have a double-V or U-groove on both sides Should be bevelled to a single-V or U-groove ANSWER DOWNLOAD EXAMIANS APP
Workshop Technology Thread rolling is restricted to Ferrous materials None of these Hard materials Ductile materials Ferrous materials None of these Hard materials Ductile materials ANSWER DOWNLOAD EXAMIANS APP
Workshop Technology When the dimension is expressed as, then the tolerance is 0.025 mm 0.035 mm 0.06 mm 0.01 mm 0.025 mm 0.035 mm 0.06 mm 0.01 mm ANSWER DOWNLOAD EXAMIANS APP
Workshop Technology Spot welding is used for welding Lap joints in plates having 0.025 mm to 1.25 mm thickness Lap joints in plates having thickness above 3 mm Butt joints in plates having 0.025 mm to 1.25 mm thickness Butt joints in plates having thickness above 3 mm Lap joints in plates having 0.025 mm to 1.25 mm thickness Lap joints in plates having thickness above 3 mm Butt joints in plates having 0.025 mm to 1.25 mm thickness Butt joints in plates having thickness above 3 mm ANSWER DOWNLOAD EXAMIANS APP