In orthogonal turning of a low carbon steel bar of diameter 150 mm with uncoated carbide tool, the cutting velocity is 90 m/min. The feed is 0.24 mm/rev and the depth of cut is 2 mm. The chip thickness obtained is 0.48 mm. If the orthogonal rake angle is zero and the principle cutting edge angle is 90⁰, the shear angle in degree is

Manufacturing And Production Technology
In orthogonal turning of a low carbon steel bar of diameter 150 mm with uncoated carbide tool, the cutting velocity is 90 m/min. The feed is 0.24 mm/rev and the depth of cut is 2 mm. The chip thickness obtained is 0.48 mm. If the orthogonal rake angle is zero and the principle cutting edge angle is 90⁰, the shear angle in degree is

30.56

20.56

36.56

26.56

30.56

20.56

36.56

26.56

ANSWER DOWNLOAD EXAMIANS APP

Manufacturing And Production Technology
If the diameter of the hole is subject to considerable variation, then for locating in jigs and fixtures, the pressure type of locator used is

Vee locator

Conical locator

Diamond pin locator

Cylindrical locator

Vee locator

Conical locator

Diamond pin locator

Cylindrical locator

ANSWER DOWNLOAD EXAMIANS APP

Manufacturing And Production Technology
The abrasive slurry used in ultrasonic machining contains fine particles of

Boron carbide

Aluminium oxide

All of the listed here

Silicon carbide

Boron carbide

Aluminium oxide

All of the listed here

Silicon carbide

ANSWER DOWNLOAD EXAMIANS APP

Manufacturing And Production Technology
The in-feed grinding is used to

All of these

Grind shoulders and formed surfaces

Grind long, slender shafts or bars

Produce tapers

All of these

Grind shoulders and formed surfaces

Grind long, slender shafts or bars

Produce tapers

ANSWER DOWNLOAD EXAMIANS APP

Manufacturing And Production Technology
In a metal arc welding process, a gas metal arc welding with magnetized flux is used and can be done in all the positions i.e. flat position, vertical position or inclined position.

Dip transfer

Spray transfer

Globular transfer

GMAW practice

Dip transfer

Spray transfer

Globular transfer

GMAW practice

ANSWER DOWNLOAD EXAMIANS APP

Manufacturing And Production Technology
The primary purpose of a sprue in a casting mould is to

Feed the casting at a rate consistent with the rate of solidification

Help feed the casting until all solidification takes place

Act as a reservoir for molten metal

Feed molten metal from the pouring basin to the gate

Feed the casting at a rate consistent with the rate of solidification

Help feed the casting until all solidification takes place

Act as a reservoir for molten metal

Feed molten metal from the pouring basin to the gate

ANSWER DOWNLOAD EXAMIANS APP

Manufacturing And Production Technology

Manufacturing And Production Technology If the diameter of the hole is subject to considerable variation, then for locating in jigs and fixtures, the pressure type of locator used is

Manufacturing And Production Technology The abrasive slurry used in ultrasonic machining contains fine particles of

Manufacturing And Production Technology The in-feed grinding is used to

Manufacturing And Production Technology In a metal arc welding process, a gas metal arc welding with magnetized flux is used and can be done in all the positions i.e. flat position, vertical position or inclined position.

Manufacturing And Production Technology The primary purpose of a sprue in a casting mould is to

Manufacturing And Production Technology
If the diameter of the hole is subject to considerable variation, then for locating in jigs and fixtures, the pressure type of locator used is

Manufacturing And Production Technology
The abrasive slurry used in ultrasonic machining contains fine particles of

Manufacturing And Production Technology
The in-feed grinding is used to

Manufacturing And Production Technology
In a metal arc welding process, a gas metal arc welding with magnetized flux is used and can be done in all the positions i.e. flat position, vertical position or inclined position.

Manufacturing And Production Technology
The primary purpose of a sprue in a casting mould is to