Refractory Technology Graphite or carbon refractories Are not resistant to corrosion by slag Should be used in neutral or reducing atmosphere Exhibit high shrinkage on thermal treatment Exihibit wetting characteristics Are not resistant to corrosion by slag Should be used in neutral or reducing atmosphere Exhibit high shrinkage on thermal treatment Exihibit wetting characteristics ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Maximum shrinkage in volume occurring during burning/firing of dried refractories may be as high as __________ percent. 15 30 20 10 15 30 20 10 ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Fireclay refractories Combine with salts (e.g. chlorides sulphates etc.) & bases (e.g. lime, magnesia etc.) forming fusible aluminates silicates etc All of these Shrink during firing Are not resistant to the action of basic slags Combine with salts (e.g. chlorides sulphates etc.) & bases (e.g. lime, magnesia etc.) forming fusible aluminates silicates etc All of these Shrink during firing Are not resistant to the action of basic slags ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology 'Super refractories' are made from pure Carbides Nitrides Oxides Borides Carbides Nitrides Oxides Borides ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology SiO₂ percentage in firebrick is about >94 35-40 55-60 80-85 >94 35-40 55-60 80-85 ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Silica refractories Have lower thermal conductivity than fireclay bricks Crack when subjected to sudden change of temperature Can not be used in the dome of hot blast stoves All of these Have lower thermal conductivity than fireclay bricks Crack when subjected to sudden change of temperature Can not be used in the dome of hot blast stoves All of these ANSWER DOWNLOAD EXAMIANS APP