Refractory Technology Fireclay bricks are never used in the Zinc roaster Coke oven walls Lead blast furnace Beehive oven Zinc roaster Coke oven walls Lead blast furnace Beehive oven ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Magnesite refractories are generally not used in the Steel melting furnace Burning zone of cement kilns Open hearth furnace Electric furnace walls Steel melting furnace Burning zone of cement kilns Open hearth furnace Electric furnace walls ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Addition of grog in fireclay brick during its manufacture is advantageous, because it results in Less shrinkage in heating, decreased apparent porosity & increased specific gravity All of these High strength & thermal spalling resistance Less addition of water to get a workable plasticity & lesser time required for drying the raw refractories and hence increased rate of production Less shrinkage in heating, decreased apparent porosity & increased specific gravity All of these High strength & thermal spalling resistance Less addition of water to get a workable plasticity & lesser time required for drying the raw refractories and hence increased rate of production ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Thoria is an expensive refractory material and is radioactive in nature. Thorium oxide is used in the manufacture of Muffles for muffle furnaces Crucibles used for melting of high purity metals Insulating bricks Segar cones Muffles for muffle furnaces Crucibles used for melting of high purity metals Insulating bricks Segar cones ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Maximum alumina content in high alumina refractory can be as high as __________ percent. 70 30 90 50 70 30 90 50 ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Crushing strength of a refractory Increases with rise in service temperature Decreases with increase in porosity Decreases with rise in service temperature Is unaffected with change in service temperature Increases with rise in service temperature Decreases with increase in porosity Decreases with rise in service temperature Is unaffected with change in service temperature ANSWER DOWNLOAD EXAMIANS APP