Engineering Materials Eutectoid reaction occurs at 1147°C 1493°C 600°C 723°C 1147°C 1493°C 600°C 723°C ANSWER DOWNLOAD EXAMIANS APP
Engineering Materials In a hardening process, the hypo-eutectoid steel is Heated from 30°C to 50°C above the upper critical temperature and then cooled slowly in the furnace Heated from 30°C to 50°C above the upper critical temperature and then cooled suddenly in a suitable cooling medium Heated from 30°C to 50°C above the upper critical temperature and then cooled in still air Heated below or closes to the lower critical temperature and then cooled slowly Heated from 30°C to 50°C above the upper critical temperature and then cooled slowly in the furnace Heated from 30°C to 50°C above the upper critical temperature and then cooled suddenly in a suitable cooling medium Heated from 30°C to 50°C above the upper critical temperature and then cooled in still air Heated below or closes to the lower critical temperature and then cooled slowly ANSWER DOWNLOAD EXAMIANS APP
Engineering Materials Compressive strength of grey cast iron in tonnes/cm is of the order of 1015 35 57 710 1015 35 57 710 ANSWER DOWNLOAD EXAMIANS APP
Engineering Materials Maximum percentage of carbon in ferrite is 0.001 0.00025 0.0006 0.0025 0.001 0.00025 0.0006 0.0025 ANSWER DOWNLOAD EXAMIANS APP
Engineering Materials Steel containing ferrite and pearlite is Soft Hard and tough Hard Tough Soft Hard and tough Hard Tough ANSWER DOWNLOAD EXAMIANS APP
Engineering Materials Wrought iron Cannot stand sudden and excessive shocks Is a ductile material Can be easily forged or welded All of these Cannot stand sudden and excessive shocks Is a ductile material Can be easily forged or welded All of these ANSWER DOWNLOAD EXAMIANS APP