Refractory Technology Refractoriness under loads (RUL) is quite close to the fusion temperature (PCE) for __________ bricks. Very low alumina Silica Dolomite Fireclay Very low alumina Silica Dolomite Fireclay ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Zircon refractories have High RUL (1600°C) and refractoriness (> 2000°C) Low co-efficient of expansion High spalling resistance All of these High RUL (1600°C) and refractoriness (> 2000°C) Low co-efficient of expansion High spalling resistance All of these ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology With decrease in porosity, the __________ of the refractories decreases. None of these Spalling resistance Strength Thermal conductivity None of these Spalling resistance Strength Thermal conductivity ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Hot face insulating linings of high purity alumina fused mullite are used, where Very high temperatures are involved All of these Presence of iron or silica is harmful Highly reducing conditions are involved Very high temperatures are involved All of these Presence of iron or silica is harmful Highly reducing conditions are involved ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Graphite or carbon refractories Exhibit high shrinkage on thermal treatment Are not resistant to corrosion by slag Should be used in neutral or reducing atmosphere Exihibit wetting characteristics Exhibit high shrinkage on thermal treatment Are not resistant to corrosion by slag Should be used in neutral or reducing atmosphere Exihibit wetting characteristics ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Pure bauxite is the best raw material for the manufacture of high alumina refractories, in which maximum alumina content can be as high as __________ percent. 80 90 55 70 80 90 55 70 ANSWER DOWNLOAD EXAMIANS APP