Engineering Materials Drop forging dies contain carbon of the order of 0.1 to 0.2% 0.7 to 0.9% 0.25 to 0.5% 0.6 to 0.7% 0.1 to 0.2% 0.7 to 0.9% 0.25 to 0.5% 0.6 to 0.7% ANSWER DOWNLOAD EXAMIANS APP
Engineering Materials The charge of the blast furnace consists of Calcined ore (8 parts), coke (4 parts) and limestone (1 part) Calcined ore (4 parts), coke (1 part) and limestone (8 parts) Calcined ore (1 part), coke (8 parts) and limestone (4 parts) Calcined ore, coke and limestone all in equal parts Calcined ore (8 parts), coke (4 parts) and limestone (1 part) Calcined ore (4 parts), coke (1 part) and limestone (8 parts) Calcined ore (1 part), coke (8 parts) and limestone (4 parts) Calcined ore, coke and limestone all in equal parts ANSWER DOWNLOAD EXAMIANS APP
Engineering Materials Grey cast iron has High tensile strength Low compressive strength Carbon in the form of free graphite All of these High tensile strength Low compressive strength Carbon in the form of free graphite All of these ANSWER DOWNLOAD EXAMIANS APP
Engineering Materials In process annealing, the hypo eutectoid steel is Heated from 30°C to 50°C above the upper critical temperature and then cooled suddenly in a suitable cooling medium Heated from 30°C to 50°C above the upper critical temperature and then cooled slowly in the furnace Heated from 30°C to 50°C above the upper critical temperature and then cooled in still air Heated below or closes to the lower critical temperature and then cooled slowly Heated from 30°C to 50°C above the upper critical temperature and then cooled suddenly in a suitable cooling medium Heated from 30°C to 50°C above the upper critical temperature and then cooled slowly in the furnace Heated from 30°C to 50°C above the upper critical temperature and then cooled in still air Heated below or closes to the lower critical temperature and then cooled slowly ANSWER DOWNLOAD EXAMIANS APP
Engineering Materials The toughness of a material __________ when it is heated. Remain same Decreases Increases None of these Remain same Decreases Increases None of these ANSWER DOWNLOAD EXAMIANS APP
Engineering Materials The temperature at which ferromagnetic alpha iron transforms to paramagnetic alpha iron is 910°C 1050°C Below recrystallization temperature 770°C 910°C 1050°C Below recrystallization temperature 770°C ANSWER DOWNLOAD EXAMIANS APP