Refractory Technology Chrome magnesite brick is not used for lining the Bottom hearth of reheating furnace Coke oven regenerator Hearth of soaking pits Burning zone of limestone rotary kilns Bottom hearth of reheating furnace Coke oven regenerator Hearth of soaking pits Burning zone of limestone rotary kilns ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Chromite refractories are Acidic refractory Basic refractory Neutral refractory Fired at a temperature of 600°C only Acidic refractory Basic refractory Neutral refractory Fired at a temperature of 600°C only ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Hot face insulating linings of high purity alumina fused mullite are used, where Highly reducing conditions are involved All of these Very high temperatures are involved Presence of iron or silica is harmful Highly reducing conditions are involved All of these Very high temperatures are involved Presence of iron or silica is harmful ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Silica refractories Have lower thermal conductivity than fireclay bricks Crack when subjected to sudden change of temperature All of these Can not be used in the dome of hot blast stoves Have lower thermal conductivity than fireclay bricks Crack when subjected to sudden change of temperature All of these Can not be used in the dome of hot blast stoves ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Mullite is chemically represented by Al2O₃ . SiO₂ 3Al2O₃ . 2SiO₂ Al2O₃ . 2SiO₂ 2Al2O₃ . 3SiO₂ Al2O₃ . SiO₂ 3Al2O₃ . 2SiO₂ Al2O₃ . 2SiO₂ 2Al2O₃ . 3SiO₂ ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Addition of grog in fireclay brick during its manufacture is advantageous, because it results in All of these Less addition of water to get a workable plasticity & lesser time required for drying the raw refractories and hence increased rate of production Less shrinkage in heating, decreased apparent porosity & increased specific gravity High strength & thermal spalling resistance All of these Less addition of water to get a workable plasticity & lesser time required for drying the raw refractories and hence increased rate of production Less shrinkage in heating, decreased apparent porosity & increased specific gravity High strength & thermal spalling resistance ANSWER DOWNLOAD EXAMIANS APP